硫酸铜和乳酸，
用氢氧化钠调Ph值到9
这怎么实现的，铜离子水溶液，稍偏碱性一些就会发生沉淀了啊


Adv. Mater. 2009, 21, 3012–3015
Fabrication of Three-Dimensional Photonic Crystals
Using Multibeam Interference Lithography and
Electrodeposition

Electrodeposition: Electrodeposition of Cu2O[31] was performed using a
conventional three-electrode setup. A platinum plate and a Ag/AgCl in
saturated potassium chloride aqueous solution (SSE) were used as counter
and reference electrodes, respectively. The electrolyte was an aqueous
solution containing cupric sulfate (0.2 M) and lactic acid (1.6 M). The pH of
the solution was adjusted to 9 by addition of sodium hydroxide. The
solution temperature was kept constant at 65 8C during deposition. The
Cu2O layer was grown under potentiostatic conditions at _0.55 V versus
SSE. To facilitate infilling of the hydrophobic SU-8 template with the cupric
sulfate aqueous solution, the 3D template was first wetted by ethanol
before electrodeposition.
--
FROM 218.249.29.149

但是加氢氧化钠的时候产生了不少的沉淀

这个配置过程怎么才能避免沉淀？
【 在 synsun (沈阳南) 的大作中提到: 】
: 有乳酸也许配合了？反正柠檬酸可以
--
FROM 218.249.29.149

应该是这样
滴加NaoH，局部浓度会过高
乳酸络合的铜离子就会析出

【 在 soccerboy (soccer) 的大作中提到: 】
: 我发现所有的电解液都是这么配的
: 但是我尝试了一次
: 先配的硫酸铜和乳酸
: ...................
--
FROM 155.69.197.*

查了，很多涉及到铜的电沉积的都有类似的配方
不知道如何配的

【 在 MSWindows7 (Operating System) 的大作中提到: 】
: 你的意思是应该用氨水来调节吗?
: NaOH用极其稀的溶液? 极其快速的搅拌?
: 这个可以请教作者一下
: ...................
--
FROM 218.249.29.149

谁给个建议吧

我怎么配都配不出来啦

搅拌的够剧烈了，还是沉淀
【 在 soccerboy (soccer) 的大作中提到: 】
: 标  题: Re: 硫酸铜、乳酸、氢氧化钠调节pH到9，怎么配能避免沉淀？
: 发信站: 水木社区 (Sat Apr  3 15:30:32 2010), 站内
:
: 給个建议，该怎么配？
: 【 在 oldgunner (放牛老农※排骨男) 的大作中提到: 】
: 应该是这样
: 滴加NaoH，局部浓度会过高
: 乳酸络合的铜离子就会析出
: